Mosi2 Heating Element, Ready For Shipment~

Product Introduction

Mosi2 Heating Element is made of molybdenum disilicide, which is resistant to high temperature and oxidation. When used in a high temperature oxidizing atmosphere, a bright and dense quartz (SiO2) glass film is formed on the surface, which can protect the inner layer of the silicon molybdenum rod from oxidation. The silicon molybdenum rod element has unique high temperature oxidation resistance.

Physical and chemical properties
Density: 5.6~5.8g/cm3
Flexural strength: 20MPa (20℃)
Vickers hardness (HV): 570kg/mm2
Porosity: 0.5~2.0%
Water absorption: 0.5%
Thermal elongation: 4%
Radiative coefficient: 0.7~0.8 (800~2000℃)

Application

Mosi2 Heating Element products are widely used in metallurgy, steelmaking, glass, ceramics, refractory materials, crystals, electronic components, semiconductor materials research, production and manufacturing, etc., especially for the production of high-performance precision ceramics, high-grade artificial crystals, precision structural metal ceramics, glass fiber, optical fiber and high-grade alloy steel.